K20 Cemented Tungsten Carbide Blanks High Hardness And Resistance
Tungsten Carbide Blanks are mainly made from tungsten carbide and cobalt powder as raw materials, through metallurgical mixing, crushing, ball grinding, pressing, sintering. The main components of alloys are WC and Co, and the content of WC and Co in different uses is different, so they are widely used. It is named for its rectangular plate (or square), also known as the tungsten carbide plate.
Technological Process of Tungsten Carbide Blanks
Pulverization → formulation according to application requirements → wet grinding → mixing → crushing → drying → screening → adding molding agent → re drying → preparing mixture after screening → granulation → pressing → forming → sintering → forming (blank) → flaw detection → packaging → warehousing.
Tungsten Carbide Blanks Garde & Technical Parameters
| Grade | Co% | Hardness
HAR | Density
g/cm | Flexural strength
MPa | Elastic modulus
GPa | Thermal expansion coefficient
10/C | Application |
| JX10 | 10 | 91.7 | 14.4 | 4300 | 490 | 5.4 | Copper, aluminum and other thin sheets with thickness less than 0.2mm |
| JX15 | 12 | 92.5 | 14.1 | 4500 | 460 | 5.8 | Copper, aluminum, stainless steel, etc |
| JX20 | 13 | 90.6 | 14.1 | 4100 | 460 | 5.8 | Strong applicability, copper, aluminum and other thin sheets |
| JX35A | 12 | 89.8 | 14.2 | 3400 | 470 | 5.7 | Q195, SPCC and other cold rolled sheets |
| JX36 | 15 | 89.4 | 13.8 | 3900 | 430 | 6.3 | EI, SPCC and other cold rolled sheets |
| JX40A | 12 | 88.9 | 14.2 | 3300 | 470 | 5.7 | Q195, SPCC and other cold rolled plates, high-speed stamping dies and multi station progressive dies |
| JX45A | 15 | 87.9 | 13.9 | 3200 | 440 | 6.1 | Die for silicon steel sheet, cold rolled sheet, hardware and standard parts |
| JX55 | 20 | 86.4 | 13.5 | 3100 | 390 | 6.8 | Silicon steel sheet, upper and lower punches |
Tungsten Carbide Blanks Picture:
Performance characteristics of Tungsten Carbide Blanks
Tungsten carbide blanks have excellent hardness, high hardness, good wear resistance, high elastic modulus, high compressive strength, chemical stability (acid resistance, alkali resistance, high temperature oxidation resistance), low impact toughness, low expansion coefficient, good heat resistance, etc.
Scope of application
Tungsten carbide blanks are mainly used in the manufacture of copper, aluminum, stainless steel, cold rolled plate, EI plate, Q195, SPCC, silicon steel plate, hardware, standard parts, high-speed up and down mold, multi-working station stage inlet mold punch and other plates. It is also the preferred material for manufacturing high temperature parts, wear resistance parts, shielding parts and corrosion resistance parts.